Product Description
A 2.0 mil white, stretchable, non-oriented cast polypropylene (CPP) film, coated on both sides with a 1.15 mil high grade synthetic hot melt rubber adhesive. This 4.3 mil tape is provided on a white, bi-siliconized paper release liner and wound on a 3” neutral core.
APPLICATIONS:
- Used for core start-ups, splicing, holding, joining, attaching, mounting and laminating.
- Ideal for splicing and laminating difficult-to-stick substrates.
- Great tack & stretchable (high elongation) properties allow the tape to adhere & conform to a variety of surfaces – smooth, rough, flat or curved.
PHYSICAL PROPERTIES:
|
Backing |
2.0 mils (0.050mm) White Cast Polypropylene |
|
Adhesive (exposed & liner side combined) |
2.3 mils (0.060mm) Synthetic Hot Melt Rubber |
|
Total Thickness (exclusive of liner) |
4.3 mils (0.110mm) |
|
Liner |
2.1 mils Bi-Siliconized Paper |
|
Adhesion to Steel |
70.6 oz/inch |
|
Tensile Strength |
5.2 lbs/inch |
|
Elongation |
800% |
|
Application Temperature |
50°F to 104°F (Optimal Range 64°F to 104°F) |
|
Temperature Resistance |
-4°F to 140°F (Optimal Range 14°F to 140°F) |
SURFACE PREPARATION:
The surface should be clean, dry, and free from grease, oil, powder, dust, release agents, etc.
STORAGE:
Tape should be stored out of direct sunlight in a cool, dry area at 65°F to 70°F and 50% RH.
Alternative to Int’l Tape #850; Tesa #64622.
NOTE: The physical properties listed above are typical test results obtained from a series of laboratory tests and should not be used for the purpose of writing specifications. Before using this product, user shall determine the suitability of the product for his/her use; and user assumes all risks and liabilities in connection therewith. All test procedures used are in accordance with ASTM and PSTC methods
Specifications
- Weight: 17 lb